POLYFLON™ M-112

About
Daikin- Polyflon™ M-112 is a modified polytetrafluoroethylene virgin granular fine cut resin. This next generation molding powder has been specifically designed for use in small to large billet compression molding. It is particularly well suited for flex applications, such as diaphragms and bellows, that require an extended service life compared to that of conventional PTFE. It exhibits excellent creep resistance and weldability characteristics.&&

About

Daikin- Polyflon™ M-112 is a modified polytetrafluoroethylene virgin granular fine cut resin. This next generation molding powder has been specifically designed for use in small to large billet compression molding. It is particularly well suited for flex applications, such as diaphragms and bellows, that require an extended service life compared to that of conventional PTFE. It exhibits excellent creep resistance and weldability characteristics.&&

Product Description
Supplier	Daikin Fluorochemicals
Generic	PTFE
Material Status	Commercial: Active
Features	No viscosity,Good flexibility,High Viscosity,Low coefficient of friction,High molecular weight,Solvent resistance,Welding,Low temperature strength
Availabilitys	North America,Asia Pacific
Process Methods	sintering

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	2.16	g/cm³	ASTM D792
Bulk density	0.36	g/cm³	ASTM D4894
Shrinkage rate
MD	0.046	%	ASTM D995
The lifespan of MIT bending	2.7E+7		ASTM D2178
Tensile void index	40.0		ASTM D4895

MECHANICAL	Nominal value	Unit	Test method
tensile strength
23℃	40	MPa	ASTM D638
compressive strength	28.3	MPa	ASTM D695
compressive strength	4.7	MPa	ASTM D695
compressive strength	7.7	MPa	ASTM D695
Tensile strain
Fracture, 23 ℃	430	%	ASTM D638
Load deformation	12.9	%	ASTM D621
Load deformation	24.9	%	ASTM D621
Load deformation	17.7	%	ASTM D621
Compression deformation	4.8	%	ASTM D621
Compression deformation	8.7	%	ASTM D621
Compression deformation	5.0	%	ASTM D621

THERMAL	Nominal value	Unit	Test method
Melting temperature	323	℃	DSC
Continuous use temperature	260	℃
Vicat Softening Temp

Electrical performance	Nominal value	Unit	Test method
Volumetric resistance	>1.0E+18	Ω.cm	ASTM D257
Surface resistance	>1.0E+15	Ω.cm	ASTM D257
Insulation strength
	3300	KV/mm	ASTM D149
Dielectric constant
	<2.10	1 kHz	ASTM D150
Dissipation factor
	<1.0E-4		ASTM D150

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level
	0.067mm	V-0	UL 94
	0.75mm	V-0	UL 94

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.