| glass/mineral filled PPS, good strength, hydrolytic stability, dimensional stability, excellent heat and chemical resistance&& |
| Product Description | |
|---|---|
| Supplier | Polygen |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Hydrolysis stability,High Heat Resistance,Solvent resistance,V-0 |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.75 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.40 | % | ISO 294-4 |
| MD | 0.20 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.020 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 150 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 1.2 | % | ISO 527-2 |
| Bending modulus | 14000 | MPa | ISO 178 |
| bending strength | 220 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 9.0 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 265 | ℃ | ISO 75-2/A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 to 140 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 290 to 320 | °C | |
| Mold temperature | 130 to 150 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |