| About |
|---|
| Product Description | |
|---|---|
| Supplier | CHI MEI |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good surface appearance |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| proportion | |||
| 23℃ | 1.125 | ASTM D792 | |
| Melt Flow Rate | |||
| 200℃，5.0kg | 1.6 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 3.2mm，6mm/min | 47.1 | MPa | ASTM D-638 |
| Tensile strain | |||
| 3.2mm，6mm/min | 30 | % | ASTM D-638 |
| Rockwell hardness | |||
| R-level | 114 | ASTM D785 | |
| Bending elasticity | |||
| 6.4mm，2.8mm/min | 2450 | MPa | ASTM D-790 |
| bending strength | |||
| 6.4mm，2.8mm/min | 70.6 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| 3.2mm，50℃/hr | 103 | ℃ | ASTM D1525 |
| Hot deformation temperature | |||
| 6.4mm，120℃/hr | 98 | ℃ | ASTM D648 |
| 6.4mm，120℃/hr | 86 | ℃ | ASTM D648 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | |||
| 23℃，3.2mm | 98 | J/m | ASTM D256 |
| 23℃，6.4mm | 118 | J/m | ASTM D256 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |