| About |
|---|
| POLYLAC® PA-747S是一种丙烯腈丁二烯苯乙烯(ABS)产品,。 它可以通过挤出进行加工,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。 特性包括: 阻燃/额定火焰 通过 ROHS 认证&& |
| Product Description | |
|---|---|
| Supplier | CHI MEI |
| Generic | ABS |
| Material Status | Commercial: Negative |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.03 | g/cm³ | ASTM D792 |
| 23℃ | 1.04 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 0.50 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 220℃，10 kg | 2.50 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.40 to 0.70 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 28 | kJ/m² | ISO 179 |
| 23℃ | 39 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 400 | J/m | ASTM D256 |
| 23℃，6.4mm | 350 | J/m | ASTM D256 |
| -30℃ | 26 | kJ/m² | ISO 180-1A |
| 23℃ | 37 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 85.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 83.0 | ℃ | ISO 75-2/A |
| 1.8 MPa, annealed | 95.0 | ℃ | ASTM D648 |
| 1.8 MPa, annealed | 99.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| — | 103 | ℃ | ASTM D1525 7 |
| A50 | 106 | ℃ | ISO 306/A50 |
| B50 | 101 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD | 9.1E-5 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 102 | ASTM D785 | |
| tensile strength | |||
| yield | 38.1 | MPa | ASTM D638 |
| yield | 41.0 | MPa | ISO 527-2/50 |
| fracture | 30.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 40 | % | ASTM D638 |
| fracture | 25 | % | ISO 527-2/50 |
| Bending modulus | |||
| — | 2070 | MPa | ASTM D790 |
| — | 1700 | MPa | ISO 178 |
| bending strength | |||
| — | 60.7 | MPa | ASTM D790 |
| — | 61.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| extrusion | Nominal value | Unit | Test method |
| drying temperature | 80 to 85 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Temperature of material cylinder zone 1 | 190 to 210 | °C | |
| Temperature of material cylinder zone 3 | 210 to 240 | °C | |
| Temperature of material cylinder zone 5 | 220 to 250 | °C | |
| Mouth temperature | 200 to 250 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |