| About |
|---|
| Product Description | |
|---|---|
| Supplier | CHI MEI |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Volume Rate | |||
| 200℃，5 kg | 4.5 | cm³/10min | ISO 1133 |
| 220℃，10 kg | 47 | cm³/10min | ISO 1133 |
| Mass density | |||
| 23℃ | 1.17 | g/cm^3 | ISO 1183 |
| proportion | |||
| 23℃ | 1.17 | ASTM D790 | |
| hardness | |||
| 1/2” | 102 | R | ASTM D792 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 20 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 19 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 92 | ℃ | ISO 306 |
| Hot deformation temperature | |||
| Unannealed | 72 | ℃ | ISO 75-2 |
| annealing | 85 | ℃ | ISO 75-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| bending strength | |||
| 1/4” , 2.8mm/min | 640 | kg/cm² | ASTM D790 |
| Bending elasticity | |||
| 1/4” , 2.8mm/min | 23000 | kg/cm² | ASTM D790 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| ALL | 1.5HB | mm | UL 94 |
| 2.5V-0 | mm | UL 94 | |
| 3.0V-0 | mm | UL 94 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |