| About |
|---|
| Product Description | |
|---|---|
| Supplier | CHI MEI |
| Material Status | Commercial: Negative |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 200℃，5.0kg | 1.8 | cm³//10min | ISO 1133 |
| 200℃，10kg | 18 | cm³/10min | ISO 1133 |
| Density | |||
| 23℃ | 1.04 | ASTM D792 | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 50 mm/min | 46 | MPa | ISO 527 |
| Tensile strain | |||
| 50 mm/min | 20 | % | ISO 527 |
| bending strength | |||
| 2 mm/min | 69 | MPa | ISO 178 |
| Bending strain | |||
| 2 mm/min | 2.4 | GPa | ISO 178 |
| Rockwell hardness | 116 | R Scale | ASTM D785 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | |||
| 23℃，4mm | 18 | kJ/m² | ISO 180 |
| Charpy impact strength | |||
| 23℃，4mm | 20 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| vicat softening point | |||
| 10N，50℃/hr | 103 | ℃ | ISO 306 |
| Hot deformation temperature | |||
| 1.8MPa, annealed | 98 | ℃ | ISO 75-2 |
| 1.8MPa, unannealed | 83 | ℃ | ISO 75-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.5mm | HB | UL 94 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |