| About |
|---|
| POLYLAN AG15E1 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Europe. Characteristics include: Flame Rated High Gloss&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good surface appearance,HB |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ASTM D1238 , ISO 1133 | ||
| 200℃，10.0kg | 20 | g/10min | ASTM D1238，ISO 1133 |
| 200℃，5.0kg | 1.8 | g/10min | ASTM D1238，ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，6.4mm | 140 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 12.7 mm | 88.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 88.0 | ℃ | ISO 75-2/A |
| 1.8 MPa, annealed, 12.7 mm | 100 | ℃ | ASTM D648 |
| 1.8 MPa, annealed | 100 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 103 | ℃ | ISO 306/A , ASTM D1525 2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 110 | ASTM D785 | |
| R-level | 110 | ISO 2039-2 | |
| Tensile modulus | |||
| 23℃ | 2750 | MPa | ASTM D638 , ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 52.0 | MPa | ASTM D638 , ISO 527-2 |
| bending strength | |||
| 23℃ | 86.0 | MPa | ASTM D790 , ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |