Polylink Polymer P-21020-T (IM)

About
Filled Polypropylene compounds are manufactured by compounding Polypropylene with fine fillers (i.e. mica, chalk, talc, glass). Additives like antioxidants, lubricant, processing aid and desiccant are added to improve long term thermal and processability. The compounds used directly or diluted with desired grades of polypropylenes show good dispensability and excellent balance of properties in the ultimate product. The fillers in the compound incorporates certain important properties those are essential for ultimate product. The modification are as below.&&

About

Filled Polypropylene compounds are manufactured by compounding Polypropylene with fine fillers (i.e. mica, chalk, talc, glass). Additives like antioxidants, lubricant, processing aid and desiccant are added to improve long term thermal and processability. The compounds used directly or diluted with desired grades of polypropylenes show good dispensability and excellent balance of properties in the ultimate product. The fillers in the compound incorporates certain important properties those are essential for ultimate product. The modification are as below.&&

Product Description
Generic	Polyolefin Elastomer
Material Status	Commercial: Active
Features	High impact resistance,Homopolymer
Availabilitys	Africa & Middle East
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.10	g/cm³	Internal Method
Melt Flow Rate
190℃，2.16kg	6.5	g/10min	ASTM D1238
Moisture content	< 600	ppm	Internal Method

MECHANICAL	Nominal value	Unit	Test method
tensile strength
fracture	17.2	MPa	ASTM D638
Tensile strain
fracture	12	%	ASTM D638
Bending modulus	2550	MPa	ASTM D790
bending strength	44.1	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	150 to 690	J/m	ASTM D256

Process Conditions
Extrusion	Nominal value	Unit	Test method
Drying temperature	70	°C
Drying time	0.50	hr
Barrel 1 zone temperature	190	°C
Barrel 2 zone temperature	200	°C
Barrel 3 zone temperature	210	°C
Barrel 4 zone temperature	215	°C
Barrel 5 zone temperature	220	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.