| Filled Nylon Compound are manufactured by compounding nylon 6 with specially treated chopped glass and modified with additives to make the compound suitable for high mechanical properties, and heat resistance. Good Weathering resistance Excellent chemical resistance. Easy processibility. Fast cycle time. Easy mould release&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good liquidity |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 to 1.38 | g/cm³ | Internal Method |
| Water absorption rate | |||
| 24hr | < 2.0 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 44 to 54 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | > 165 | ℃ | ASTM D648 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 110 | ASTM D785 | |
| tensile strength | |||
| fracture | 71.1 to 90.7 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 5.0 | % | ASTM D638 |
| Bending modulus | 5690 to 6080 | MPa | ASTM D790 |
| bending strength | 115 to 140 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 to 100 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel 1 zone temperature | 190 | °C | |
| Barrel 2 zone temperature | 220 | °C | |
| Barrel 3 zone temperature | 230 | °C | |
| Barrel 4 zone temperature | 220 | °C | |
| Barrel 5 zone temperature | 220 to 240 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Dev 5 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |