| About |
|---|
| POLYNIL® P36/4 is an unreiforced Polyamide 66 (Nylon 66) for compounding and alloying. This general pourpose 2.4 viscosity Polyamide 66 resin is FDA compliant. POLYNIL® P36/4 has moisture content lower than 0.4%.&& |
| Product Description | |
|---|---|
| Supplier | Nilit |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | V-2 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ISO 1183 |
| Water absorption rate | ISO 62 | ||
| 23℃，24hr | 1.5 | % | ISO 62 |
| Saturation, 23 ℃ | 8.5 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 3100 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 81.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 50 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 2850 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 120 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 4.5 | kJ/m² | ISO 179/1eA |
| 23℃ | 5.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 | ISO 179/1eU | |
| Impact strength of cantilever beam notch | ISO 180/A | ||
| -30℃ | 4.5 | kJ/m² | ISO 180-A |
| 23℃ | 5.5 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 225 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 72.0 | ℃ | ISO 75-2/A |
| Continuous use temperature | 85.0 | ℃ | IEC 60216 |
| Vicat Softening Temp | 240 | ℃ | ISO 306/B |
| Ball pressure test | IEC 60695-10-2 | ||
| 125℃ | 通过 | IEC 60695-10-2 | |
| 165℃ | 通过 | IEC 60695-10-2 | |
| Melting temperature | 258 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 2 mm | 18 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | |||
| 3.20 mm, solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | V-2 | UL 94 | |
| 3.20 mm | V-2 | UL 94 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 0.80 mm | 750 | ℃ | IEC 60695-2-12 |
| 3.2 mm | 850 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 0.8 mm | 775 | ℃ | IEC 60695-2-13 |
| 3.2 mm | 750 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 28 | % | ISO 4589-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 20000 hr |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |