| 4002EPG(+) flame retardant PA66 is halogen free environmental polyamide material with nitrogen and phosphorus as flame retardant elements, with 30% glass filled. Carbonize, expansion and physical cooling mechanism play the flame retardant performance. 4002EPG(+) halogen free flame retardant PA66 flammability reach UL94V-0(1.5mm), glow wire test meets GWIT750°C and GWFI960°C. It has the characteristics of low density, great electrical property, low smoke and no corrosion to molds etc.&& |
| Product Description | |
|---|---|
| Supplier | POLYROCKS |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Low smoke,Good Electrical Properties,Halogen free,Flame Characteristics,Low density |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.43 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 275℃，2.16kg | 10 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.20 | % | |
| TD | 0.70 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 120 | MPa | ASTM D638 |
| Bending modulus | 8300 | MPa | ASTM D790 |
| bending strength | 170 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 80 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 240 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glowing wire flammability index | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | 750 | ℃ | IEC 60695-2-13 |
| Notes |
|---|
| 1. Nitrogen and Phosphorus |
| 2. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |