| About |
|---|
| Product characteristics Very good weldirg and processing properties Flame retardant High rigidity Product applications Ventilation industry Chemical engineering and tank building&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Flame Characteristics,Welding,Homopolymer |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.940 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | < 0.10 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 81.0 | ℃ | ISO 306/B |
| Melting temperature | 162 to 167 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 1.2E-4 to 1.9E-4 | 1/℃ | DIN 53752 |
| specific heat | 1700 | J/kg/℃ | DIN 52612 |
| Thermal conductivity coefficient | 0.20 | W/m/K | DIN 52612 |
| Operating temperature | |||
| long-term | 0 to 100 | ℃ | |
| short-term | < 150 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | > 15 | kV/mm | IEC 60243-1 |
| Dielectric constant | 2.30 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 1.9E-4 | IEC 60250 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 3.00 mm | V-2 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 70 | ISO 868 | |
| Tensile modulus | 1300 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 32.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 50 | % | ISO 527-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |