| About |
|---|
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good stripping performance |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | |
| Water absorption rate | 0.1 | % | |
| Shrinkage rate | |||
| MD | 0.45 | % | |
| Melt Flow Rate | |||
| MD | 2.5 | g/10min | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 52.0 | MPa | |
| Tensile modulus | 3300 | MPa | |
| Tensile strain | |||
| fracture | 2 | % | |
| Tensile creep modulus | |||
| 1 hour | 3300 | MPa | |
| 1000 hrs | 2600 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.3 | J/cm² | |
| Charpy Unnotch Impact strength | 0.3 | J/cm² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | |||
| TD：20℃ | 8E-5 | /℃ | |
| Hot deformation temperature | |||
| 0.45 MPa | 84 | ℃ | |
| 1.8 MPa | 76 | ℃ | |
| Vicat Softening Temp | 89 | ℃ | |
| Glass transition temperature | 90 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 18 | % | |
| Flame retardant level | |||
| 3.20 mm | HB | UL 94 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | ≥1.00e+15 | ohms·cm | |
| Surface resistivity | 1.00e+14 | ohms/sq | |
| Dielectric constant | |||
| 100 Hz | 2.5 | ||
| 1 MHz | 2.5 | ||
| Dissipation factor | |||
| 100 Hz | 0.000090 | ||
| 1 MHz | 0.000070 | ||
| Compared to the leakage tracing index | 375 | V |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |