| About |
|---|
| Polytron P40N037 is Natural, 40% Long Glass Fiber Reinforced, Heat Stabilized,UV Stabilized POLYPROPYLENE, The Glass Fibers are Chemically Coupled to the Polymer Matrix, The material is supplied in pellets that are typically 12mm in length. Fiber length is the length of the pellets. Typical applications include Structural Automotive Applications , For Exterior Applications |
| Product Description | |
|---|---|
| Supplier | Ram-On |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Chemical coupling,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD：2.0 mm | 0.25 to 0.30 | % | |
| TD：2.0 mm | 0.10 to 0.15 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 9000 | MPa | |
| 70℃ | 6000 | MPa | |
| Tensile stress | |||
| — | 115 | MPa | |
| 150°C | 75.0 | MPa | |
| Tensile strain | |||
| fracture | 2.2 | % | |
| Fracture, 150 ℃ | 2.7 | % | |
| Bending modulus | 9000 | MPa | ISO 178 |
| Bending stress | 165 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| — | 26 | kJ/m² | |
| -40℃ | 29 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| — | 65 | kJ/m² | |
| -40℃ | 75 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 158 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 156 | ℃ | ISO 75-2/A |
| Melting temperature | 168 | ℃ | ISO 11357-3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.00 mm | HB | UL 94 | |
| Flammability | < 100 | mm/min | FMVSS 302 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Temperature at the rear of the barrel | 230 to 250 | °C | |
| Temperature in the middle of the barrel | 230 to 250 | °C | |
| Front temperature of material barrel | 230 to 250 | °C | |
| Mold temperature | 50 to 70 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |