| PVC Compound Low Impact Strength E-1826-PL, natural colour compound, has an balance stiffness and impact resist, designed for extrussion profile (edge bending) Features Low Impact Strength Processing Methode Extrussion Typical Applications Profile (edge bending)&& |
| Product Description | |
|---|---|
| Generic | PVC, not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific,Europe |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | ASTM D792 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 220 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 53.8 | ℃ | ASTM D648 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 76 | ASTM D2240 | |
| tensile strength | 58.8 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 180 | % | ASTM D638 |
| Rockwell hardness | |||
| R-level | 14 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Hopper temperature | 150 to 155 | °C | |
| Barrel 1 zone temperature | 150 to 155 | °C | |
| Barrel 2 zone temperature | 155 to 160 | °C | |
| Barrel 3 zone temperature | 155 to 160 | °C | |
| Barrel 4 zone temperature | 160 to 165 | °C | |
| Barrel 5 zone temperature | 165 to 170 | °C | |
| Connector temperature | 160 to 165 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |