| About |
|---|
| PVC Compound Low Impact Strength M-1828-GL, High clarity with total clear, has an balance stiffness and impact resist, designed for bottle application under 300 ml (Depend design and wall thickness of the bottle) Features Low Impact Strength High Clarity Processing Methode Blow Molding Typical Applications Bottle&& |
| Product Description | |
|---|---|
| Generic | PVC, not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Clarity,High impact resistance |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ASTM D792 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 76 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 55.2 | ℃ | ASTM D648 |
| Vicat Softening Temp | 81.6 | ℃ | ASTM D256 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | 3.4 | mm/min | ASTM D635 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | 90.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 81 | ASTM D2240 | |
| tensile strength | 58.8 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 180 | % | ASTM D638 |
| Rockwell hardness | |||
| R-level | 17 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Hopper temperature | 160 to 170 | °C | |
| Barrel 1 zone temperature | 160 to 170 | °C | |
| Barrel 2 zone temperature | 170 to 180 | °C | |
| Barrel 3 zone temperature | 180 to 185 | °C | |
| Barrel 4 zone temperature | 185 to 190 | °C | |
| Barrel 5 zone temperature | 185 to 190 | °C | |
| Nozzle temperature | 185 to 195 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |