POOYATAK CG203

About
Cling MB Description POOYATAK CG203 is a PE based master batch containing a tackifying resin is used as a cling agent. It can be used in LLDPE or LDPE based stretch wrap and cling wrap films for pallet wrapping, silage wrapping and food packaging whether by blown or cast processing. The agent migrates to the film surface within 24 to 72 hours and exhibits the cling properties by then. There must neither be any slip or antiblock agent in the film base resin nor as masterbatch in the formulas. Application POOYATAK CG203 is designed for ease of dilution and homogeneous mixing and is therefore suitable for direct addition using automatic dosing units or by pre-blending. Depending on the film thickness (the thicker film needs less addition level), process (the blown process needs double dosage), film cooling temperature (higher cooling temperature needs more level) and the final application it can be used from 2 to 10%. It should be stored in a dry and cool place not to exceed 6 month.&&

About

Cling MB Description POOYATAK CG203 is a PE based master batch containing a tackifying resin is used as a cling agent. It can be used in LLDPE or LDPE based stretch wrap and cling wrap films for pallet wrapping, silage wrapping and food packaging whether by blown or cast processing. The agent migrates to the film surface within 24 to 72 hours and exhibits the cling properties by then. There must neither be any slip or antiblock agent in the film base resin nor as masterbatch in the formulas. Application POOYATAK CG203 is designed for ease of dilution and homogeneous mixing and is therefore suitable for direct addition using automatic dosing units or by pre-blending. Depending on the film thickness (the thicker film needs less addition level), process (the blown process needs double dosage), film cooling temperature (higher cooling temperature needs more level) and the final application it can be used from 2 to 10%. It should be stored in a dry and cool place not to exceed 6 month.&&

Product Description
Generic	PE
Material Status	Commercial: Active
Features	High adhesion degrees
Availabilitys	Africa & Middle East ,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.910	g/cm³	ASTM D1505
Melt Flow Rate
120℃，1.20kg	5.0 to 11	g/10min	ASTM D1238
Moisture content	< 2000	ppm	ASTM D644

Supplementary information	Nominal value	Unit	Test method
Particle size	40.0 to 50.0	pcs/cm³	Internal Method

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.