| 20%玻纤增强，高刚性，低收缩，高机械强度，耐热性。纱管，泵浦外壳，控制器外壳，家电 产品零件，风扇叶片等。 强化 PP 因具有价格低廉、成形容易、机械强度均衡、电气性质优良、耐水、耐热水性 优良等特性。但是在不同的产品结构设计与肉厚下，强度、配向性、收缩率、产品翘曲 度等影响更需考虑。 |
| Product Description | |
|---|---|
| Supplier | Nan Ya |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Electrical Properties,Low or no water absorption,Quick molding cycle,Low density,Heat Resistance, Good,Good Rigidity |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Melt Flow Rate | 4 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.2~0.4 | % | ASTM D955 |
| TD | 0.5~0.8 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 73.5 | MPa | ASTM D638 |
| bending strength | 2744 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notch impact strength (3.2mm) | 68.6 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa | 158 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Insulation failure strength (3.2mm) | 40 | Kv/mm | ASTM D149 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| drying temperature | 100 | ℃ | |
| Drying time | 1~2 | hrs | |
| Nozzle temperature | 190~210 | ℃ | |
| Front temperature | 185~205 | ℃ | |
| Mid section temperature | 180~190 | ℃ | |
| Post stage temperature | 170~180 | ℃ | |
| Mold temperature | 50~70 | ℃ | |
| Injection pressure | 40~90 | MPa | |
| Screw speed | 180~210 | rpm | |
| Injection speed | 快速 | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |