| About |
|---|
| AF-312C is specifically engineered to meet the need for high performance products in the flame retardant resin applications. AF-312C provides an optimum balance of physical properties, high heat resistance,outstanding UV stability and good finished part aesthetics.&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good surface appearance,Flame Characteristics,High Heat Resistance,V-0 |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 200℃，5.0kg | 5.1 | g/10min | ASTM D1238 |
| 220℃，10.0kg | 53 | g/10min | ASTM D1238 |
| 230℃，3.80kg | 17 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 22000 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 43.4 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| yield | 5.0 | % | ASTM D638 |
| fracture | 20 | % | ASTM D638 |
| Bending modulus | 27000 | MPa | ASTM D790 |
| bending strength | 71.1 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | ASTM D256 | ||
| -30℃，3.2 mm | 78 | J/m | ASTM D256 |
| -30℃，6.4 mm | 78 | J/m | ASTM D256 |
| 23℃，3.2 mm | 280 | J/m | ASTM D256 |
| 23℃，6.4 mm | 250 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 88.0 | ℃ | ASTM D648 |
| 0.45 MPa, annealed, 6.4 mm | 83.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 76.0 | ℃ | ASTM D648 |
| 1.8 MPa, annealed, 6.4 mm | 84.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 84.0 | ℃ | ASTM D1525 4 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.59 in/min |
| 4. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |