| About |
|---|
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Burn residue | 0 | % | ASTM D5630 |
| Density | 0.93 | g/cm³ | ASTM D792 |
| Water absorption rate | 0.03 | % | ASTM D570 |
| Shrinkage rate | |||
| MD | – | % | ASTM D995 |
| TD | – | % | ASTM D995 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 98 | R 级 | ASTM D785 |
| tensile strength | 34 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 12 | % | ASTM D638 |
| bending strength | 39 | MPa | ASTM D790 |
| Bending modulus | 1580 | MPa | ASTM D790 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | – | Ohm | IEC 60093 |
| Dielectric strength | – | KV/mm | IEC 60243 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa | 126 | ℃ | ASTM D648 |
| melting point | 165 | ℃ | ASTM D649 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 16.5 | g/10min | ASTM D1238 |
| Scorching hot wire | GWIT：750/3.0 | IEC 60695-2-13 | |
| Flame retardant level | |||
| V2 | 1.5mm | UL 94 | |
| V2 | 3.0mm | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | – | kJ/m² | ASTM D250 |
| Charpy Notched Impact Strength | |||
| 23℃ | 4.8 | kJ/m² | ASTM D250 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |