PPO JB110+LT - SOLIAO

About

Product Description
Supplier	Polysyron
Generic	PPO(PPE)+PS
Material Status	Commercial: Active
Features	Good flexibility,High ESCR

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Shrinkage rate	0.5-0.7	%	ISO 294-4
Density	1.05	g/cm³	ISO 1183-1
Melt Flow Rate
280℃，5.0kg	15	g/10min	ISO1133

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa	124	℃	ISO 75-2
Flame retardant level	HB		UL 94

MECHANICAL	Nominal value	Unit	Test method
bending strength	75	MPa	ISO 178
Tensile strain	35	%	ISO 527
tensile strength	55	MPa	ISO527
Bending modulus	2400	MPa	ISO178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	20	KJ/m²	ISO180

Process Conditions
Typical processing conditions	Nominal value	Unit	Test method
Melt temperature	240-280	℃
Mold temperature	一般不用加
Rear section of barrel temperature	240-260	℃
Middle section of barrel temperature	250-270	℃
Front section of barrel temperature	260-280	℃
Injection molding speed	中高速
Back pressure	5-10MPa	MPa
Drying temperature	100-110	℃
Drying time	2-4	h
Processing upper limit temperature	290	℃

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.