| About |
|---|
| PRE-ELEC® CP 1515 is a carbon black filled conductive thermoplastic compound based on polyolefin copolymer. In addition to a low electrical resistivity. PRE-ELEC® CP 1515 has an excellent balance of mechanical properties and is easy to extrude. PRE-ELEC® CP 1515 has been developed especially for block-process foams.&& |
| Product Description | |
|---|---|
| Supplier | Premix Oy |
| Generic | 聚烯烃，共挤薄膜用聚烯烃 |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Conductive |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.05 | g/cm³ | ASTM D792 |
| — | 1.06 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ASTM D1238 , ISO 1133 | ||
| 190℃，21.6kg | 50 | g/10min | ASTM D1238，ISO 1133 |
| 190℃，5.0kg | 1.2 | g/10min | ASTM D1238，ISO 1133 |
| Shrinkage rate | |||
| MD | 1.2 | % | ASTM D955 |
| MD | 1.2 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 , ASTM D256 | ||
| -20℃ | 40 | kJ/m² | ASTM D256，ISO 179 |
| 23℃ | 无断裂 | ISO 179 , ASTM D256 | |
| Charpy Unnotch Impact strength | |||
| -20℃ | 无断裂 | ISO 179 , ASTM D256 | |
| 2℃ | 无断裂 | ISO 179 | |
| 23℃ | 无断裂 | ASTM D256 | |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -20℃，4mm | 无断裂 | ASTM D256 | |
| 23℃，4mm | 无断裂 | ASTM D256 | |
| Impact strength of cantilever beam notch | ISO 180 | ||
| 23℃ | 无断裂 | ISO 180 | |
| Notched impact strength of cantilever beam | ASTM D256 | ||
| -20℃，4 mm | 无断裂 | ASTM D256 | |
| 23℃，4 mm | 无断裂 | ASTM D256 | |
| Notched impact strength of cantilever beam | ISO 180 | ||
| -20℃ | 无断裂 | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 35.0 | ℃ | ASTM D648，ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 50.0 | ℃ | ASTM D1525，ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | < 1.0E+3 | ohms | ESD STM11.11，IEC 61340-2-3 |
| Volume resistivity | < 1.0E+2 | ohms·cm | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 , ISO 868 | ||
| Shaw’s A | 95 | ASTM D2240 , ISO 868 | |
| Shaw’s D | 50 | ASTM D2240 , ISO 868 | |
| tensile strength | 11.0 | MPa | ASTM D638 , ISO 527-2 |
| Tensile strain | |||
| fracture | 450 | % | ASTM D638 , ISO 527-2 |
| Bending modulus | |||
| 4 mm | 1100 | MPa | ASTM D790 |
| 4 mm | 110 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 60 | °C | |
| Drying time | 3.0 | hr | |
| Barrel 1 zone temperature | 180 | °C | |
| Barrel 2 zone temperature | 180 | °C | |
| Barrel 3 zone temperature | 190 | °C | |
| Barrel 4 zone temperature | 190 | °C | |
| Barrel 5 zone temperature | 200 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 4 mm thickness |
| 3. 4 mm thick |
| 4. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |