| About |
|---|
| PRE-ELEC® PE 1296 is a conductive thermoplastic concentrate based on PE-HD. Conductivity is achieved by using a special conductive carbon black. PRE-ELEC® PE 1296 contains a high load of carbon black and it can be diluted up to 50% with virgin or recycled PE-HD. The actual amount should always be tested as it also depends on the processing conditions. Typical applications for PRE-ELEC® PE 1296 include blow moulded canisters and containers and mono- or co-extruded pipes and sheets. It can also be used in injection molding.&& |
| Product Description | |
|---|---|
| Supplier | Premix Oy |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Conductive,High density |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.11 | g/cm³ | ASTM D792 |
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，21.6kg | 0.60 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 2.5 to 3.5 | % | ASTM D955 |
| MD | 2.5 to 3.5 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shaw’s A | 95 | ISO 868 | |
| Shaw’s D | 65 | ISO 868 | |
| tensile strength | 13.1 | MPa | ASTM D638 |
| yield | 24.0 | MPa | ISO 527-2 |
| 4 mm | 13.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 4 mm | 40 | % | ISO 527-2 |
| yield | 12 | % | ISO 527-2 |
| Bending modulus | |||
| 4 mm | 1200 | MPa | ASTM D790 |
| 4 mm | 1200 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -20℃ | 61 | kJ/m² | ASTM D256 |
| -20℃ | 60 | kJ/m² | ISO 179 |
| 23℃ | 65 | kJ/m² | ISO 179 |
| 23℃ | 67 | kJ/m² | ASTM D256 |
| Charpy Unnotch Impact strength | |||
| -20℃ | No Break | ASTM D256 | |
| -20℃ | No Break | ISO 179 | |
| 2℃ | No Break | ISO 179 | |
| 23℃ | No Break | ASTM D256 | |
| -20℃，4.00 mm | 60.9 | kJ/m² | ASTM D256 |
| 23℃，4.00 mm | 73.6 | kJ/m² | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180 | ||
| Area | ASTM D256 | ||
| -20℃ | 60 | kJ/m² | ISO 180 |
| 23℃ | 71 | kJ/m² | ISO 180 |
| Notched impact strength of cantilever beam | ASTM D256 | ||
| -20℃，4 mm | No Break | ASTM D256 | |
| 23℃，4 mm | No Break | ASTM D256 | |
| Notched impact strength of cantilever beam | ISO 180 | ||
| -20℃ | No Break | ISO 180 | |
| 23℃ | No Break | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 43.3 | ℃ | ASTM D648-A |
| 1.8 MPa, unannealed | 43.0 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed | 76.7 | ℃ | ASTM D648-B |
| 0.45 MPa, unannealed | 77.0 | ℃ | ISO 75-2/Bf |
| Vicat Softening Temp | |||
| — | 129 | ℃ | ASTM D1525 4 |
| — | 76.1 | ℃ | ASTM D1525 5 |
| Vicat Softening Temp | |||
| A50 | 129 | ℃ | ISO 306/A50 |
| B50 | 73.0 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | < 1.0E+5 | ohms | ESD STM11.11 |
| Surface resistivity | < 1.0E+5 | ohms | IEC 61340-2-3 |
| Volume resistivity | < 1.0E+3 | ohms·cm | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 60 to 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 210 to 250 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Injection pressure | 60.0 to 80.0 | MPa | |
| Injection speed | Moderate | ||
| Drying temperature | 60 to 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel 1 zone temperature | 200 | °C | |
| Barrel 2 zone temperature | 210 | °C | |
| Barrel 3 zone temperature | 220 | °C | |
| Barrel 4 zone temperature | 220 | °C | |
| Barrel 5 zone temperature | 230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 4 mm thickness |
| 3. 4 mm thick |
| 4. Rate A (50°C/h), Loading 2 (50 N) |
| 5. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |