| PREPERM® L335 is a special compound with elevated dielectric constants of 3.35. PREPERM® L335 is based on Premix proprietary PPE technology. Extremely low dissipation factor (0.0005) makes PREPERM® L335 an excellent material for high frequency applications. PREPERM® L335 offers stable dielectric constant over wide frequency and wide temperature range. PREPERM® retains its physical properties at very low (-78°C) temperatures. PREPERM® L335 can be injection moulded or extruded. Applications include structural parts for antennas in base stations, point to point, wlan, mobile phones etc. Devices made out of PREPERM® L335 can operate at very high frequencies as PREPERM® L335 offers stable performance even at 120 GHz.&& |
| Product Description | |
|---|---|
| Supplier | Premix Oy |
| Generic | PPO(PPE) |
| Material Status | Commercial: Active |
| Features | Low temperature toughness,Low temperature strength,V-1 |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 | g/cm³ | |
| Melt Flow Rate | |||
| 300℃，5.0kg | 18 | g/10min | ISO 1133 |
| Shrinkage rate | 1.0 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ISO 527-2 | ||
| yield | 55.0 | MPa | ISO 527-2 |
| 4 mm | 45.0 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| yield | 8.0 | % | ISO 527-2 |
| Fracture, 4 mm | 25 | % | ISO 527-2 |
| Bending modulus | |||
| 4 mm | 2100 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180 | ||
| -78℃ | 16 | kJ/m² | ISO 180 |
| -20℃ | 20 | kJ/m² | ISO 180 |
| 23℃ | 无断裂 | ISO 180 | |
| Notched impact strength of cantilever beam | ISO 180 | ||
| -78℃ | 无断裂 | ISO 180 | |
| -20℃ | 无断裂 | ISO 180 | |
| 23℃ | 无断裂 | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 177 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed | 155 | ℃ | ISO 75-2/Af |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | |||
| 1.00 GHz | 3.35 | Internal Method | |
| Dissipation factor | |||
| 1 GHz | 5.0E-4 | Internal Method |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 4.00 mm | V-1 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 120 to 140 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 290 to 310 | °C | |
| Mold temperature | 80 to 140 | °C | |
| Injection pressure | 60.0 to 80.0 | MPa | |
| Drying temperature | 120 to 140 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Melt temperature | 260 to 280 | °C | |
| Nozzle temperature | 260 to 300 | °C | |
| Traction roller | 60 to 180 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 4 mm thickness |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |