| Improved productivity and reliability. Nonchlorinated, nonbrominated flame retardant. 180F HDT.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | |
| TD | 0.50 to 0.70 | % | |
| Water absorption rate | |||
| 24hr | 0.060 | % | ASTM D570 |
| Outdoor applicability | f1 | UL 746C | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 59.0 | MPa | |
| fracture | 41.0 | MPa | |
| Tensile strain | |||
| yield | 6.7 | % | |
| fracture | 23 | % | |
| Bending modulus | |||
| 100 mm span | 2340 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 100 mm span | 82.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 270 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak | 35.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 91.0 | ℃ | |
| 1.8 MPa, unannealed, 6.4 mm | 82.0 | ℃ | |
| Vicat Softening Temp | 112 | ℃ | ASTM D1525 6 |
| Relative temperature index | 95.0 | ℃ | UL 746 |
| Electrical performance | 95.0 | ℃ | UL 746 |
| Impact mechanical performance | 80.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Volume resistivity | 7.6E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 3.2 mm in oil | 18 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 60 Hz | 2.85 | ||
| 50 kHz | 2.85 | ||
| 1 MHz | 2.63 | ||
| Dissipation factor | |||
| 50 Hz | 0.012 | ||
| 60 Hz | 0.012 | ||
| 1 MHz | 7.0E-3 | ||
| Arc resistance | PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 1 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 1 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 4 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 2 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 | |
| Radiation Plate Listing | TRUE |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 65 to 90 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 210 to 245 | °C | |
| Barrel middle temperature | 215 to 260 | °C | |
| Barrel front temperature | 220 to 265 | °C | |
| Nozzle temperature | 230 to 270 | °C | |
| Processing (melt) temperature | 230 to 270 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 25 to 75 | rpm | |
| Vent depth | 0.038 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. Type I, 2.0 in/min |
| 4. 0.10 in/min |
| 5. Rate A (50°C/h), Loading 2 (50 N) |
| 6. Tungsten Electrode |
| 7. Surface |
| 8. UL Tested |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |