| About |
|---|
| PRIMACOR™ 3003 Copolymer is an ethylene acrylic acid copolymer which has been specifically designed by SK for use as an adhesive or sealant layer in extrusion coating and extrusion lamination. PRIMACOR 3003 Copolymer exhibits: Excellent draw-down and edge stability Excellent organoleptic properties Excellent toughness and strength Outstanding environmental stress crack and product resistance Excellent hot-tack and sealability Adhesion to paper, paperboard, metals and polyethylenes Insensitivity to moisture Applications: Flexible packaging laminates Liquid packaging board laminates Complies with: U.S. FDA 21 CFR 177.1310(a)(1) EU, No 10/2011 Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | EAA |
| Material Status | Commercial: Negative |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.935 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 7.8 | g/10min | ASTM D1238，ISO 1133 |
| Co monomer content | 6.5 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 2% secant | 130 | MPa | ASTM D638 , ISO 527-2 |
| tensile strength | ASTM D638 , ISO 527-2 | ||
| yield | 7.50 | MPa | ASTM D638 , ISO 527-2 |
| fracture | 18.0 | MPa | ASTM D638 , ISO 527-2 |
| Tensile strain | |||
| fracture | 590 | % | ASTM D638 , ISO 527-2 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Initial sealing temperature | 90.0 | ℃ | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 90.0 | ℃ | ISO 306/A |
| Melting temperature | |||
| DSC | 100 | ℃ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 260 to 290 | °C | |
| Shrinkage 5 (290癈) | 45.7 | mm | |
| Minimum coating weight (290癈) | 8.0 | g/m² | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Comonomer content measured by a proprietary method that has equivalent accuracy as compared to ASTM D 4094. |
| 3. 25 g/m² coatings at 290°C set temperature. |
| 4. at 100 m/min, 25 g/m² coatings |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |