| About |
|---|
| PRIMACOR™ 3330 Copolymer is an ethylene acrylic acid copolymer suitable for extrusion coating and extrusion lamination applications. PRIMACOR 3330 Copolymer has been specifically designed for use as an adhesive resin for extrusion and coextrusion coating and extrusion lamination or sealant layer. PRIMACOR 3330 Copolymer exhibits: Excellent adhesion to metallic, paper and PE substrates. Excellent heat sealability and hot tack. Excellent toughness. Excellent oil and grease resistance. Insensitive to moisture. Applications: Flexible packaging laminates Plastic tube laminates Complies with: U.S. FDA 21 CFR 177.1310(a)(1) EU, No 10/2011 Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | EAA |
| Material Status | Commercial: Negative |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.932 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 5.8 | g/10min | ASTM D1238，ISO 1133 |
| Co monomer content | 6.5 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D638 , ISO 527-2 | ||
| Yield, molding | 8.34 | MPa | ASTM D638 , ISO 527-2 |
| Fracture, molded | 17.4 | MPa | ASTM D638 , ISO 527-2 |
| Tensile strain | |||
| Fracture, molded | 520 | % | ASTM D638 , ISO 527-2 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Initial sealing temperature | 92.8 | ℃ | Internal Method |
| Water vapor transmittance | |||
| 38℃，90% RH | 0.40 | g·mm/m²/atm/24 hr | DIN 53122/2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 85.0 | ℃ | ASTM D1525 , ISO 306 |
| Melting temperature | |||
| DSC | 100 | ℃ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 260 to 290 | °C | |
| Shrinkage (288°C, 25.4 μm) | 50.8 | mm | |
| Minimum coating thickness | 20 | µm | |
| Minimum coating weight | 20 | g/m² | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Comonomer content measured by a proprietary method that has equivalent accuracy as compared to ASTM D 4094. |
| 3. 25 g/m² coatings at 290°C set temperature. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |