| Low heat seal temperature, high hot tack High gloss, excellent clarity Excellent grease and oil resistance, water hold-out and excellent product resistance for flexible packaging applications Complies with: U.S. FDA 21 CFR 177.1310(a)(2) Consult the regulations for complete details. PRIMACOR™ 5980I is an ethylene acrylic acid copolymer with excellent adhesion to metallic, cellulosic, glass and other polar substrates. In dispersion form, it can be used effectively as a foil primer or laminating adhesive for polyethylene and metallized substrates. Applications: Adhesives Laminations Foil priming Heat sealing Nonwoven binding Metal/paper coating Outstanding Properties: Dispersible in aqueous amines and alkali “Clean” dispersion requires no salts, surfactants or solvents Dispersions use existing waterbourne application equipment High hot tack Low odor&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | EAA |
| Material Status | Commercial: Negative |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.958 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | ASTM D1238 , ISO 1133 | ||
| 125℃，2.16kg | 14 | g/10min | ASTM D1238，ISO 1133 |
| 190℃，2.16kg | 300 | g/10min | ASTM D1238，ISO 1133 |
| Co monomer content | 20.5 | % | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 42.2 | ℃ | ASTM D1525 , ISO 306 |
| Melting temperature | |||
| DSC | 77.2 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 50 | ASTM D2240 , ISO 868 | |
| Tensile modulus | |||
| 2% cut, molded | 33.1 | MPa | ASTM D638 , ISO 527-2 |
| tensile strength | |||
| Fracture, molded | 9.65 | MPa | ASTM D638 , ISO 527-2 |
| Tensile strain | |||
| Fracture, molded | 390 | % | ASTM D638 , ISO 527-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. As measured at the time of production. |
| 3. Melt Index values are correlated from Melt Flow Rate (ASTM D 1238 conditions of 125°C/2.16kg). |
| 4. Comonomer content measured by a proprietary method that has equivalent accuracy as compared to ASTM D 4094. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |