PRIMACOR™ 5990I

About
Low heat seal temperature, high hot tack High gloss, excellent clarity Excellent water, grease and oil resistance Complies with U.S. FDA 21 CFR 177.1310(a)(2) PRIMACOR™ 5990I is an ethylene acrylic acid copolymer with excellent adhesion to metallic, cellulosic, glass and other substrates. In dispersion form, it is a versatile binder for nonwoven fibers, including polypropylene, polyester, glass, nylon and others. Applications: Adhesives Laminations Foil priming Heat sealing Nonwoven binding Metal/paper coating Outstanding Properties: Dispersible in aqueous amines and alkali “Clean” dispersion requires no salts, surfactants or solvents Dispersions use existing waterbourne application equipment High hot tack Low odor&&

About

Low heat seal temperature, high hot tack High gloss, excellent clarity Excellent water, grease and oil resistance Complies with U.S. FDA 21 CFR 177.1310(a)(2) PRIMACOR™ 5990I is an ethylene acrylic acid copolymer with excellent adhesion to metallic, cellulosic, glass and other substrates. In dispersion form, it is a versatile binder for nonwoven fibers, including polypropylene, polyester, glass, nylon and others. Applications: Adhesives Laminations Foil priming Heat sealing Nonwoven binding Metal/paper coating Outstanding Properties: Dispersible in aqueous amines and alkali “Clean” dispersion requires no salts, surfactants or solvents Dispersions use existing waterbourne application equipment High hot tack Low odor&&

Product Description
Supplier	DOW
Generic	EAA
Material Status	Commercial: Negative
Availabilitys	North America,Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.955	g/cm³	ASTM D792 , ISO 1183
Melt Flow Rate			ASTM D1238 , ISO 1133
125℃，2.16kg	65	g/10min	ASTM D1238，ISO 1133
190℃，2.16kg	1300	g/10min	ASTM D1238，ISO 1133
Co monomer content	20.0	%	Internal Method

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
2% cut, molded	22.1	MPa	ASTM D638 , ISO 527-2
tensile strength
Fracture, molded	6.21	MPa	ASTM D638 , ISO 527-2
Tensile strain
Fracture, molded	350	%	ASTM D638 , ISO 527-2

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	40.0	℃	ASTM D1525 , ISO 306
Melting temperature
DSC	75.0	℃	Internal Method

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.