Prime ABS 750 Is a general purpose ABS product that has good impact strength, and good hot strength for thermoforming. It is an amorphous thermoplastic material and therefore, processes easier than some other thermoplastic materials. Applications: Prime ABS 750 may be used for interior applications such as appliance parts, tub and shower wall surrounds, and interior automotive trim. With the addition of a weatherable cap it may also be used in many outdoor applications. Processing: Prime ABS 750 is rather easy to thermoform due to its exceptional hot strength. It can be formed on wood, epoxy, ceramic and or aluminum tools. The forming temperature has a range of 300 -350°F. For best results the mold temperature should be 150-190°F. In some cases it is necessary to dry the sheet before forming. Finishing: Parts made with Prime ABS 750 may be joined with machine screws, bolts, nuts, rivets, and spring steel fasteners. Thread cutting or thread-forming screws is an economical means of securing separate joints. Formed parts may be joined with Methylene Chloride if maximum impact strength is not required. Press and snap techniques and sonic welding may also be used for the bonding of Prime ABS 750. Please contact your Primex Plastics representative for more information on finishing, fabricating, or the thermoforming process. Colors, Textures, Capabilities: Prime ABS 750 can be color matched to meet your specific requirements. Prime ABS 750 is available in Thicknesses from .030 – .400. Textures include; Calf Grain, HC, RM, Seville, Levant I, FL/HC and Diamond Plate.&&

About

Prime ABS 750 Is a general purpose ABS product that has good impact strength, and good hot strength for thermoforming. It is an amorphous thermoplastic material and therefore, processes easier than some other thermoplastic materials. Applications: Prime ABS 750 may be used for interior applications such as appliance parts, tub and shower wall surrounds, and interior automotive trim. With the addition of a weatherable cap it may also be used in many outdoor applications. Processing: Prime ABS 750 is rather easy to thermoform due to its exceptional hot strength. It can be formed on wood, epoxy, ceramic and or aluminum tools. The forming temperature has a range of 300 -350°F. For best results the mold temperature should be 150-190°F. In some cases it is necessary to dry the sheet before forming. Finishing: Parts made with Prime ABS 750 may be joined with machine screws, bolts, nuts, rivets, and spring steel fasteners. Thread cutting or thread-forming screws is an economical means of securing separate joints. Formed parts may be joined with Methylene Chloride if maximum impact strength is not required. Press and snap techniques and sonic welding may also be used for the bonding of Prime ABS 750. Please contact your Primex Plastics representative for more information on finishing, fabricating, or the thermoforming process. Colors, Textures, Capabilities: Prime ABS 750 can be color matched to meet your specific requirements. Prime ABS 750 is available in Thicknesses from .030 – .400. Textures include; Calf Grain, HC, RM, Seville, Levant I, FL/HC and Diamond Plate.&&

Product Description
Generic	ABS
Material Status	Commercial: Active
Features	High impact resistance,Machinable,High Heat Resistance,Good Tensile Strength,Ultrasonic soldering,low-temperature impact resistance,Agglomerability,Amorphous,HB
Availabilitys	North America,Europe
Process Methods	Thermo forming

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.04	g/cm³	ASTM D792
Melt Flow Rate
230℃，3.80kg	1.7	g/10min	ASTM D1238

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch			ASTM D256
-40℃	120	J/m	ASTM D256
23℃	340	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, annealed	92.2	℃	ASTM D648
Vicat Softening Temp	107	℃	ASTM D1525

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
> 1.27 mm	Pass		FMVSS 302
0.76 mm	HB		UL 94

optical performance	Nominal value	Unit	Test method
gloss
60°	90		ASTM D523

Supplementary information	Nominal value	Unit
Temperature of hot forming mold
Forming Temperature	149 to 177	℃
Mold temperature	66 to 88	℃

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	102		ASTM D785
tensile strength
yield	35.2	MPa	ASTM D638
Bending modulus	1860	MPa	ASTM D790
bending strength	55.2	MPa	ASTM D790

Notes
1. Typical properties: these are not to be construed as specifications.
2. >0.03 in
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.