Prime ABS ST80

About
Is an alloy of thermoplastic elastomers and weatherable ASA co-extruded over a rigid ABS substrate. Prime ABS ST80 is designed to provide a low gloss look and soft feel, which boasts excellent durability, chemical resistance and UV stability as well as improved sound dampening. Applications: Prime ABS ST80 is particularly suited for use in exterior applications or those interior parts that will be exposed to direct UV light such as dashboards, panels and trim. This includes marine, recreational, automotive, heavy truck, agricultural and construction equipment. Processing: Prime ABS ST80 can be thermoformed on conventional equipment employing techniques typical for thermoforming ABS. Male or female tools may be used. Prime ABS ST80 should be heated only from the substrate side. As long as the substrate reaches a temperature suitable for thermoforming, the soft touch cap layer will also be hot enough to thermoform. The soft touch cap layer should not be heated to a temperature above 325°F. The best appearance and performance of the soft touch cap layer has been obtained when the sheet is thermoformed with the temperature of the cap layer at 300°F. As a general rule, heating rates of 0.5-0.75 sec/mil are the maximum recommended for thermoforming ABS. Finishing: Prime ABS ST80 can be screwed, drilled, routed, punched and die-cut with conventional tooling. Parts made with Prime ABS ST80 may be joined with machine screws, bolts, nuts, rivets, and spring steel fasteners. Threadcutting or thread-forming screws are an economical means of securing separate joints. Formed parts may be joined with Methylene Chloride if maximum impact strength is not required. Press and snap techniques and sonic welding may also be used for the bonding of Prime ABS ST80. Please contact your Primex Plastics representative for more information on finishing, fabricating, or the thermoforming process. Colors, Textures and Capabilities: Prime ABS ST80 can be color matched to meet your specific requirements. Textures include Calf Grain, HC, Seville, Levant I, and FL/HC.&&

About

Is an alloy of thermoplastic elastomers and weatherable ASA co-extruded over a rigid ABS substrate. Prime ABS ST80 is designed to provide a low gloss look and soft feel, which boasts excellent durability, chemical resistance and UV stability as well as improved sound dampening. Applications: Prime ABS ST80 is particularly suited for use in exterior applications or those interior parts that will be exposed to direct UV light such as dashboards, panels and trim. This includes marine, recreational, automotive, heavy truck, agricultural and construction equipment. Processing: Prime ABS ST80 can be thermoformed on conventional equipment employing techniques typical for thermoforming ABS. Male or female tools may be used. Prime ABS ST80 should be heated only from the substrate side. As long as the substrate reaches a temperature suitable for thermoforming, the soft touch cap layer will also be hot enough to thermoform. The soft touch cap layer should not be heated to a temperature above 325°F. The best appearance and performance of the soft touch cap layer has been obtained when the sheet is thermoformed with the temperature of the cap layer at 300°F. As a general rule, heating rates of 0.5-0.75 sec/mil are the maximum recommended for thermoforming ABS. Finishing: Prime ABS ST80 can be screwed, drilled, routed, punched and die-cut with conventional tooling. Parts made with Prime ABS ST80 may be joined with machine screws, bolts, nuts, rivets, and spring steel fasteners. Threadcutting or thread-forming screws are an economical means of securing separate joints. Formed parts may be joined with Methylene Chloride if maximum impact strength is not required. Press and snap techniques and sonic welding may also be used for the bonding of Prime ABS ST80. Please contact your Primex Plastics representative for more information on finishing, fabricating, or the thermoforming process. Colors, Textures and Capabilities: Prime ABS ST80 can be color matched to meet your specific requirements. Textures include Calf Grain, HC, Seville, Levant I, and FL/HC.&&

Product Description
Generic	ASA+ABS
Material Status	Commercial: Active
Features	Weather resistance is good,High impact resistance,noise reduction,Machinable,High Heat Resistance,Durability,Ultrasonic soldering,Solvent resistance,Soft,Agglomerability,Low Gloss
Availabilitys	North America,Europe
Process Methods	Thermo forming

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.04	g/cm³	ASTM D792
Melt Flow Rate
230℃，3.80kg	3.0	g/10min	ASTM D1238

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃，3.2mm	500	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature			ASTM D648
0.45 MPa, unannealed, 3.2 mm	93.3	℃	ASTM D648
1.8 MPa, unannealed, 3.2 mm	81.1	℃	ASTM D648
Vicat Softening Temp	105	℃	ASTM D1525
Linear coefficient of thermal expansion
MD	9.5E-5	1/℃	ASTM D696

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	1.0E+14	ohms

optical performance	Nominal value	Unit	Test method
gloss
60°	3		ASTM D523

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	53		ASTM D2240
tensile strength
Fracture, 3.18 mm	24.8	MPa	ASTM D638
Tensile strain			ASTM D638
Yield, 3.18 mm	7.0	%	ASTM D638
Fracture, 3.18 mm	10	%	ASTM D638
Bending modulus
3.18 mm, 50.80 mm span	814	MPa	ASTM D790

Notes
1. Typical properties: these are not to be construed as specifications.
2. 0.050 in/min
3. Initial
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.