Prime PETG 14471

About
Is an economical high-clarity PETG co-polyester resin developed for thick sheet applications. The benefits of this material are excellent clarity, outstanding toughness, chemical resistance, cold formable without stress whitening, machinable, excellent thermoforming characteristics and it can be sealed with adhesives. Applications: Include point of purchase, displays, store fixtures, indoor and outdoor signs, vending machine parts, and industrial, building, construction, and architectural components. Processing: Forming conditions for Prime PETG 14471 are as follows; Oven temperatures should be 400-500°F, forming temperature of sheet should be 300-330°F, mold temperature should be <120°F, de-mold the part at < 130°F. The mold should have a 3-5° draft angle to aid with the release of the part. Finishing: Techniques used for the fabricating and finishing of Prime PETG 14471 include; Cold and Hot bending, sawing, drilling, punching, shearing, and die cutting. Saw edges can be mechanically, flame or solvent polished. Prime PETG 14471 can be painted, hot stamped and is easy to bond with commercial products. Please contact your Primex Plastics representative for more information on finishing, fabricating, or the thermoforming process. Colors, Textures and Capabilities: Prime PETG 14471 can be color matched to meet your specific requirements, however, it is generally a clear product. It is available in thicknesses of .060 - .236 and up to 56" in width.&&

About

Is an economical high-clarity PETG co-polyester resin developed for thick sheet applications. The benefits of this material are excellent clarity, outstanding toughness, chemical resistance, cold formable without stress whitening, machinable, excellent thermoforming characteristics and it can be sealed with adhesives. Applications: Include point of purchase, displays, store fixtures, indoor and outdoor signs, vending machine parts, and industrial, building, construction, and architectural components. Processing: Forming conditions for Prime PETG 14471 are as follows; Oven temperatures should be 400-500°F, forming temperature of sheet should be 300-330°F, mold temperature should be <120°F, de-mold the part at < 130°F. The mold should have a 3-5° draft angle to aid with the release of the part. Finishing: Techniques used for the fabricating and finishing of Prime PETG 14471 include; Cold and Hot bending, sawing, drilling, punching, shearing, and die cutting. Saw edges can be mechanically, flame or solvent polished. Prime PETG 14471 can be painted, hot stamped and is easy to bond with commercial products. Please contact your Primex Plastics representative for more information on finishing, fabricating, or the thermoforming process. Colors, Textures and Capabilities: Prime PETG 14471 can be color matched to meet your specific requirements, however, it is generally a clear product. It is available in thicknesses of .060 - .236 and up to 56" in width.&&

Product Description
Generic	3D打印材料
Material Status	Commercial: Active
Features	Good Clarity,Good flexibility,Sprayable,Machinable,Good bond,Good Tensile Strength,Solvent resistance,High ESCR,Agglomerability,HB,V-2
Availabilitys	North America,Europe
Process Methods	Thermo forming

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.27	g/cm³	ASTM D792

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch			ASTM D256
-30℃	37	J/m	ASTM D256
23℃	91	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	69.4	℃	ASTM D648
Vicat Softening Temp	82.8	℃	ASTM D1525
Linear coefficient of thermal expansion
MD	7.2E-5	1/℃	ASTM D696

FLAME CHARACTERISTICS	Nominal value	Test method
Flame retardant level		UL 94
0.25 mm	HB	UL 94
3.00 mm	V-2	UL 94

optical performance	Nominal value	Unit	Test method
Haze	< 1.0	%	ASTM D1003

Supplementary information	Nominal value	Unit
De（mold Temperature）	< 54	℃
Mold temperature
other	< 49	℃
Oven Temperature	204 to 260	℃
Forming temperature	149 to 166	℃

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	104		ASTM D785
tensile strength
yield	53.1	MPa	ASTM D638
Tensile strain
fracture	50	%	ASTM D638
Bending modulus	2140	MPa	ASTM D790

Notes
1. Typical properties: these are not to be construed as specifications.
2. >0.01 in
3. >0.118 in
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.