| About |
|---|
| PRIME TPO F-3740 is a Polypropylene Random Copolymer (PP Random Copolymer) product. It is available in Asia Pacific, Europe, or North America. Primary characteristic: copolymer.&& |
| Product Description | |
|---|---|
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 4.5 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 80 | µm | |
| Tensile modulus | JIS Z1702 | ||
| MD，80 µm | 190 | MPa | JIS Z1702 |
| TD，80 µm | 190 | MPa | JIS Z1702 |
| tensile strength | JIS Z1702 | ||
| MD, fracture, 80 µ m | 29.0 | MPa | JIS Z1702 |
| TD, fracture, 80 µ m | 29.0 | MPa | JIS Z1702 |
| Tensile strain | JIS Z1702 | ||
| fracture | > 500 | % | ISO 527-2 |
| MD, fracture, 80 µ m | > 500 | % | JIS Z1702 |
| TD, fracture, 80 µ m | > 500 | % | JIS Z1702 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃ | 无断裂 | ISO 180 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | JIS K7105 | ||
| 80 µm | 5.5 | % | JIS K7105 |
| 80 µm | 0.60 | % | JIS K7105 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 52 | ASTM D2240 | |
| tensile strength | ISO 527-2 | ||
| yield | 8.50 | MPa | ISO 527-2 |
| fracture | 14.5 | MPa | ISO 527-2 |
| Bending modulus | 150 | MPa | ISO 178 |
| bending strength | 6.50 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Internal |
| 3. All |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |