PRIMEVA® P2430C

About
EVA resin REPSOL PRlMEVA® P2430C is recommended for injection moulding as well as for blends with other products like waxes and mineral fillers. It contains antioxidant and free flowing agent Applications: Injection moulding. Release agents containing silicone must be avoided. Blends with waxes. Manufacture of masterbatches. Microcellularfoams. Extrusion of profiles and sheets with high flexibility. Can be used to produce halogen-free-flame-retardant (HFFR) cables compounds. Recommended melt temperature below 200°C to avoid the decomposition of the polymer. Processing conditions should be optimised for each production line.

About

EVA resin REPSOL PRlMEVA® P2430C is recommended for injection moulding as well as for blends with other products like waxes and mineral fillers. It contains antioxidant and free flowing agent Applications: Injection moulding. Release agents containing silicone must be avoided. Blends with waxes. Manufacture of masterbatches. Microcellularfoams. Extrusion of profiles and sheets with high flexibility. Can be used to produce halogen-free-flame-retardant (HFFR) cables compounds. Recommended melt temperature below 200°C to avoid the decomposition of the polymer. Processing conditions should be optimised for each production line.

Product Description
Supplier	REPSOL
Generic	EVA
Material Status	Commercial: Active
Features	Food contact compliance,High Flexibility,Inoxidizability,Copolymer
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Foam extrusion molding

Technical Data
THERMAL	Nominal value	Unit	Test method
Melting temperature	77.0	℃	Internal Method
Ring and Ball Softening Point	162	°C	ASTM E28

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s A	79
Shaw’s D	29
Tensile stress (fracture)	25.0	MPa	ISO 527-2
Tensile strain
fracture	740	%	ISO 527-2

PHYSICAL	Nominal value	Unit	Test method
Density
23℃	0.944	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	3.0	g/10min	ISO 1133
Vinyl acetate content	24.0	wt%	Internal Method
Brookfield viscosity
180℃	3728000	mPa·s
200℃	6696000	mPa·s

Process Conditions
Injection	Nominal value	Unit	Test method
extrusion	Nominal value	Unit	Test method
Processing (melt) temperature	200	°C
Melt Temperature	200	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.