| About |
|---|
| EVA copolymer ALCUDIA® PA-539 is suitable for film extrusion and extrusion coating. This material combines easy processability with excellent mechanical and optical properties. It contains antioxidant additives. TYPICAL APPLICATIONS Film extrusion Extrusion coating Recommended melt temperature below 200°C to avoid the decomposition of the polymer. Processing conditions should be optimised for each production line.&& |
| Product Description | |
|---|---|
| Supplier | REPSOL |
| Generic | EVA |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Food contact compliance,Inoxidizability |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.937 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| F50 | > 300 | hr | ASTM D1693 |
| Vinyl acetate content | 18.0 | wt% | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| tensile strength | |||
| MD, fracture, 50 µ m, blow molded film | 26.0 | MPa | |
| TD, fracture, 50 µ m, blow molded film | 22.0 | MPa | |
| Tensile strain | |||
| MD, fracture, 50 µ m, blow molded film | 320 | % | |
| TD, fracture, 50 µ m, blow molded film | 640 | % | |
| Drop hammer impact | |||
| 50 µ m, blow molded film | 600 | g | ISO 7765-1 |
| Elmandorf tear strength | |||
| MD: 50 µ m, blow molded film | 2.0 | N | |
| TD: 50 µ m, blow molded film | 2.8 | N |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 64.0 | ℃ | ISO 306/A |
| Melting temperature | 87.0 | ℃ |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 50 µ m, blow molded film | 4.0 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 200 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |