| About |
|---|
| PRL PC-GP3-D-(color)-1 is a Polycarbonate (PC) product. It can be processed by injection molding and is available in North America. Characteristics include: Flame Rated RoHS Compliant Good Mold Release High Flow Mold Release Agent&& |
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High liquidity,Good stripping performance,V-2 |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 14 to 20 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 690 | J/m | ASTM D256 |
| Drop hammer impact | |||
| 3.2 mm | > 36.2 | J | ASTM D3029 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 127 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 132 | ℃ | ASTM D648 |
| Vicat Softening Temp | 149 | ℃ | ASTM D1525 2 |
| 1.5 mm | 125 | ℃ | UL 746 |
| 3.0 mm | 125 | ℃ | UL 746 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 0.75 mm | 80.0 | ℃ | UL 746 |
| 1.5 mm | 115 | ℃ | UL 746 |
| 3.0 mm | 115 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 0.75 mm | 28 | kV/mm | ASTM D149 |
| Arc resistance | PLC 5 | ASTM D495 | |
| Compared to the leakage tracing index | |||
| 0.749 mm | PLC 2 | UL 746 | |
| High Arc Burning Index (HAI) | UL 746 | ||
| 1.5 mm | PLC 0 | UL 746 | |
| 3.0 mm | PLC 1 | UL 746 | |
| High voltage arc marking rate (HVTR) (0.749 mm) | PLC 2 | UL 746 | |
| Hot wire ignition | |||
| HWI | UL 746 | ||
| 1.5 mm | PLC 2 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-2 | UL 94 | |
| 3.00 mm | V-2 | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 2540 µm | 88.0 | % | ASTM D1003 |
| Haze | |||
| 2540 µm | 1.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 3.18 mm | 68.9 | MPa | ASTM D638 |
| Yield, 3.17 mm | 62.1 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.18 mm | 120 | % | ASTM D638 |
| Yield, 3.18 mm | 6.0 | % | ASTM D638 |
| Bending modulus | |||
| 3.17 mm | 2310 | MPa | ASTM D790 |
| bending strength | |||
| 3.18 mm | 95.8 | MPa | ASTM D790 |
| Rockwell hardness | ASTM D785 | ||
| M-level | 70 | ASTM D785 | |
| R-level | 118 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 118 to 124 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Barrel rear temperature | 260 to 282 | °C | |
| Barrel middle temperature | 271 to 293 | °C | |
| Barrel front temperature | 282 to 304 | °C | |
| Processing (melt) temperature | 288 to 316 | °C | |
| Mold temperature | 71 to 93 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |