| About |
|---|
| PRL PC/TP-GP2 is a Polycarbonate + Polyester (PC+Polyester) product. It can be processed by injection molding and is available in North America. Characteristics include: Flame Rated RoHS Compliant Impact Resistant Chemical Resistant Impact Modified&& |
| Product Description | |
|---|---|
| Generic | PC + Polyester |
| Material Status | Commercial: Active |
| Features | High impact resistance,Ablation resistance,Solvent resistance,low-temperature impact resistance,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 265℃，2.16kg | 6.0 to 12 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.70 to 1.0 | % | ASTM D955 |
| MD：3.2 mm | 0.60 to 0.90 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 3.18 mm | 56.5 | MPa | ASTM D638 |
| Yield, 3.17 mm | 57.9 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.18 mm | 120 | % | ASTM D638 |
| Bending modulus | |||
| 3.17 mm | 2070 | MPa | ASTM D790 |
| bending strength | |||
| 3.18 mm | 89.6 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -40℃，3.2mm | 530 | J/m | ASTM D256 |
| 23℃，3.2mm | 850 | J/m | ASTM D256 |
| Drop hammer impact | |||
| 3.2 mm | > 36.2 | J | ASTM D3029 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 93.3 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 98.9 | ℃ | ASTM D648 |
| 1.5 mm | 75.0 | ℃ | UL 746 |
| 3.0 mm | 75.0 | ℃ | UL 746 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 1.5 mm | 75.0 | ℃ | UL 746 |
| 3.0 mm | 75.0 | ℃ | UL 746 |
| 1.5 mm | 75.0 | ℃ | UL 746 |
| 3.0 mm | 75.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 9.5E+16 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm, all colors | HB | UL 94 | |
| 3.00 mm, all colors | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 104 to 110 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Barrel rear temperature | 249 to 271 | °C | |
| Barrel middle temperature | 254 to 277 | °C | |
| Barrel front temperature | 260 to 282 | °C | |
| Processing (melt) temperature | 246 to 274 | °C | |
| Mold temperature | 66 to 88 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |