| PRL PEI-G10是一种聚醚酰亚胺(PEI)产品,含有的填充物为10% 玻璃纤维增强材料。 它可以通过注射成型进行加工,在北美洲有供货。 特性包括: 阻燃/额定火焰 通过 ROHS 认证 Flame Retardant 耐热&& |
| Product Description | |
|---|---|
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,High Heat Resistance,V-0 |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 337℃，6.60kg | 5.0 to 22 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.60 | % | ASTM D955 |
| Water absorption rate | |||
| Equilibrium, 23 ℃ | 1.2 | % | ASTM D570 |
| 24hr | 0.21 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃，3.2 mm | 480 | J/m | ASTM D4812 |
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 400 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 204 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 207 | ℃ | ASTM D648 |
| Vicat Softening Temp | 221 | ℃ | ASTM D1525 2 |
| Linear coefficient of thermal expansion | |||
| MD：-20~150℃ | 3.2E-5 | 1/℃ | ASTM E831 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 1.5 mm | 105 | ℃ | UL 746 |
| 3.0 mm | 105 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 1.59 mm in oil | 27 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 kHz | 3.50 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 1 kHz | 1.4E-3 | ASTM D150 | |
| 2 GHz | 4.6E-3 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm, all colors | V-0 | UL 94 | |
| 3.00 mm, all colors | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 3.18 mm | 4550 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, 3.18 mm | 114 | MPa | ASTM D638 |
| Yield, 3.17 mm | 114 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.18 mm | 6.0 | % | ASTM D638 |
| Bending modulus | |||
| 3.17 mm | 5100 | MPa | ASTM D790 |
| bending strength | |||
| 3.18 mm | 186 | MPa | ASTM D790 |
| Rockwell hardness | |||
| M-level | 114 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 143 to 149 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 24 | hr | |
| Barrel rear temperature | 332 to 399 | °C | |
| Barrel middle temperature | 338 to 399 | °C | |
| Barrel front temperature | 343 to 399 | °C | |
| Processing (melt) temperature | 338 to 399 | °C | |
| Mold temperature | 107 to 177 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |