| About |
|---|
| PRL PPX-EN-FR3 is a Polyphenylene Ether + PS (PPE+PS) product. It can be processed by extrusion and is available in North America. Characteristics include: Flame Rated RoHS Compliant Flame Retardant Halogen Free Heat Resistant&& |
| Product Description | |
|---|---|
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,Heat Resistance, Good,V-2,V-1 |
| Availabilitys | North America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.06 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 250℃，11.6kg | 4.0 to 8.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -40℃，3.2mm | 130 | J/m | ASTM D256 |
| 23℃，3.2mm | 210 | J/m | ASTM D256 |
| Drop hammer impact | |||
| 3.2 mm | 16.9 | J | ASTM D3029 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 121 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 129 | ℃ | ASTM D648 |
| 0.75 mm | 65.0 | ℃ | UL 746 |
| 1.5 mm | 110 | ℃ | UL 746 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 1.5 mm | 105 | ℃ | UL 746 |
| 1.7 mm | 105 | ℃ | UL 746 |
| 3.0 mm | 105 | ℃ | UL 746 |
| 1.7 mm | 110 | ℃ | UL 746 |
| 3.0 mm | 110 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 3 mm | 24 | kV/mm | ASTM D149 |
| Compared to the leakage tracing index | |||
| 0.750 mm | PLC 2 | UL 746 | |
| High Arc Burning Index (HAI) | UL 746 | ||
| 1.5 mm | PLC 1 | UL 746 | |
| 1.7 mm | PLC 1 | UL 746 | |
| 3.0 mm | PLC 1 | UL 746 | |
| High voltage arc marking rate (HVTR) (0.750 mm) | PLC 3 | UL 746 | |
| Hot wire ignition | |||
| HWI | UL 746 | ||
| 1.5 mm | PLC 0 | UL 746 | |
| 1.7 mm | PLC 0 | UL 746 | |
| 3.0 mm | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm, black | V-2 | UL 94 | |
| 1.50 mm, all colors | V-1 | UL 94 | |
| 1.70 mm, all colors | V-1 | UL 94 | |
| 3.00 mm, all colors | V-1 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 3.18 mm | 62.1 | MPa | ASTM D638 |
| Yield, 3.17 mm | 64.1 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.18 mm | 25 | % | ASTM D638 |
| Bending modulus | |||
| 3.17 mm | 2410 | MPa | ASTM D790 |
| bending strength | |||
| 3.18 mm | 89.6 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 119 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 104 to 110 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel 1 zone temperature | 204 | °C | |
| Barrel 2 zone temperature | 227 | °C | |
| Barrel 3 zone temperature | 227 | °C | |
| Melt temperature | 227 to 254 | °C | |
| Nozzle temperature | 249 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |