| About |
|---|
| PRL PPX-G30 is a Polyphenylene Ether + PS (PPE+PS) product filled with 30% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include: Flame Rated RoHS Compliant Heat Resistant Hydrolytically Stable Moisture Resistant&& |
| Product Description | |
|---|---|
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Hydrolysis stability,Low or no water absorption,High Heat Resistance,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.28 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 250℃，11.6kg | 1.0 to 8.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.10 to 0.40 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.3 | kJ/m² | ISO 179/1 |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 23℃ | 6.3 | kJ/m² | ISO 180-1A |
| -30℃，3.2mm | 53 | J/m | ASTM D256 |
| 23℃，3.2mm | 80 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 143 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 149 | ℃ | ASTM D648 |
| Vicat Softening Temp | 152 | ℃ | ASTM D1525 2 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 1.5 mm | 65.0 | ℃ | UL 746 |
| 3.0 mm | 65.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm, all colors | HB | UL 94 | |
| 3.00 mm, all colors | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 3.18 mm | 110 | MPa | ASTM D638 |
| Yield, 3.17 mm | 110 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.18 mm | 2.0 | % | ASTM D638 |
| Bending modulus | |||
| 3.17 mm | 7580 | MPa | ASTM D790 |
| bending strength | |||
| 3.18 mm | 159 | MPa | ASTM D790 |
| Rockwell hardness | |||
| Level L | 108 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 104 to 110 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Barrel rear temperature | 260 to 304 | °C | |
| Barrel middle temperature | 271 to 310 | °C | |
| Barrel front temperature | 282 to 316 | °C | |
| Processing (melt) temperature | 293 to 316 | °C | |
| Mold temperature | 82 to 116 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |