PRL PPX/NY-G20

About
PRL PPX/NY-G20 is a Polyphenylene Ether + PS + PA (PPE+PS+Nylon) product filled with 20% glass fiber. It can be processed by injection molding and is available in North America. Primary characteristic: rohs compliant.&&

Product Description
Generic	PPO(PPE)+PS+PA
Material Status	Commercial: Active
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.25	g/cm³	ASTM D792
Melt Flow Rate
300℃，3.80kg	1.0 to 4.0	g/10min	ASTM D1238
Shrinkage rate
MD：3.2 mm	0.40 to 0.70	%	ASTM D955

MECHANICAL	Nominal value	Unit	Test method
tensile strength
Fracture, 3.18 mm	114	MPa	ASTM D638
Yield, 3.17 mm	114	MPa	ASTM D638
Bending modulus
3.17 mm	5380	MPa	ASTM D790
bending strength
3.18 mm	169	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃，3.2mm	48	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed, 3.2 mm	221	℃	ASTM D648
0.45 MPa, unannealed, 3.2 mm	210	℃	ASTM D648

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	93 to 107	°C
Drying time	3.0 to 4.0	hr
Drying time, maximum	8.0	hr
Barrel rear temperature	268 to 302	°C
Barrel middle temperature	274 to 302	°C
Barrel front temperature	279 to 302	°C
Processing (melt) temperature	279 to 302	°C
Mold temperature	79 to 121	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.