| PRL PPX/NY-GP2 is a Polyphenylene Ether + PS + PA (PPE+PS+Nylon) product. It can be processed by injection molding and is available in North America. Characteristics include: RoHS Compliant Heat Resistant&& |
| Product Description | |
|---|---|
| Generic | PPO(PPE)+PS+PA |
| Material Status | Commercial: Active |
| Features | Heat Resistance, Good |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，3.80kg | 10 to 30 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.90 to 1.2 | % | ASTM D955 |
| MD：3.2 mm | 1.0 to 1.3 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃，3.2mm | 110 | J/m | ASTM D256 |
| 23℃，3.2mm | 190 | J/m | ASTM D256 |
| Drop hammer impact | |||
| 3.2 mm | 28.2 | J | ASTM D3029 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 129 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 154 | ℃ | ASTM D648 |
| Vicat Softening Temp | 199 | ℃ | ASTM D1525 2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 3.18 mm | 55.2 | MPa | ASTM D638 |
| Yield, 3.17 mm | 57.9 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.18 mm | 50 | % | ASTM D638 |
| Bending modulus | |||
| 3.17 mm | 2210 | MPa | ASTM D790 |
| bending strength | |||
| 3.18 mm | 93.1 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 116 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 93 to 107 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Barrel rear temperature | 266 to 302 | °C | |
| Barrel middle temperature | 271 to 302 | °C | |
| Barrel front temperature | 279 to 302 | °C | |
| Processing (melt) temperature | 279 to 302 | °C | |
| Mold temperature | 77 to 121 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |