| PRL PPX-SF2 is a Polyphenylene Ether + PS (PPE+PS) product. It can be processed by structural foam molding and is available in North America. Typical application: Foam. Characteristics include: Flame Rated RoHS Compliant Flame Retardant Halogen Free Heat Resistant&& |
| Product Description | |
|---|---|
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Foaming performance,Halogen free,Flame Characteristics,Self-extinguishing,Heat Resistance, Good,V-0 |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.09 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 250℃，11.6kg | 25 to 45 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.60 to 0.90 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 3.18 mm | 51.7 | MPa | ASTM D638 |
| Yield, 3.17 mm | 52.4 | MPa | ASTM D638 |
| Bending modulus | |||
| 3.17 mm | 2410 | MPa | ASTM D790 |
| bending strength | |||
| Fracture, 3.18 mm | 82.7 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 160 | J/m | ASTM D256 |
| Drop hammer impact | |||
| 3.2 mm | 16.9 | J | ASTM D3029 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 98.9 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 104 | ℃ | ASTM D648 |
| 3.0 mm | 65.0 | ℃ | UL 746 |
| 6.0 mm | 65.0 | ℃ | UL 746 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 3.0 mm | 65.0 | ℃ | UL 746 |
| 6.0 mm | 65.0 | ℃ | UL 746 |
| 3.0 mm | 65.0 | ℃ | UL 746 |
| 6.0 mm | 65.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 3.00 mm | V-0 | UL 94 | |
| 6.00 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 71 to 82 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Barrel rear temperature | 232 to 260 | °C | |
| Barrel middle temperature | 271 to 304 | °C | |
| Barrel front temperature | 271 to 304 | °C | |
| Processing (melt) temperature | 271 to 304 | °C | |
| Mold temperature | 66 to 82 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |