| About |
|---|
| Pro-fax SG722 fully formulated high impact polypropylene copolymer is available in pellet form. This resin is typically used in injection molding applications and offers very good cold temperature impact resistance. For regulatory compliance information see Pro-fax SG722 Product Stewardship Bulletin (PSB).&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good surface appearance,High impact resistance,Nucleation,Antistatic property,low-temperature impact resistance,Impact copolymer |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.902 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 25 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 22.8 | MPa | ASTM D638 |
| Tensile strain | |||
| Yield, 23 ℃ | 6.6 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 1030 | MPa | ASTM D790 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | 86 | ASTM D2457 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 93.3 | ℃ | ASTM D648 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | NB | J/m | ASTM D256 |
| Impact | >=45 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.050 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |