| About |
|---|
| Promyde B30 P2 MI is a Polyamide 6 impact modified, heat stabilised with equilibrated mechanical properties and optimal flow behaviour. CHARACTERISTICS Promyde B30 P2 MI is a polyamide 6 impact modified and heat stabilized. APPLICATIONS Promyde B30 P2 MI allows a fast and efficient mould filling, and easy mould release, that combined with its excellent mechanical and impact resistant properties make it suitable for applications sensitive to breakage by impact (e.g. housings, fittings, small parts and anchors).&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,Good liquidity,Quick molding cycle,Good stripping performance,Heat Stabilized,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 275℃，5 kg | 100 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 0.80 to 1.1 | % | |
| MD | 0.90 to 1.1 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 8.5 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 2.5 | % | ISO 62 |
| Viscosity value | |||
| H2SO4，Sulphuric Acid | 125 | cm³/g | ISO 960 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2800 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, 23 ℃ | 75.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Yield, 23 ℃ | 5.0 | % | ISO 527-2/50 |
| Nominal tensile fracture strain | |||
| 23℃ | 25 | % | ISO 527-2/50 |
| Bending modulus | |||
| 23℃ | 2300 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 85.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 12 | kJ/m² | ISO 179/1eA |
| 23℃ | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | No Break | ISO 179/1eU | |
| 23℃ | No Break | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 55.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 150 | ℃ | ISO 75-2/B |
| Melting temperature | |||
| DSC | 222 | ℃ | ISO 3146 |
| Linear coefficient of thermal expansion | |||
| TD：23~80℃ | 1.0E-4 | 1/℃ | ISO 11359-2 |
| MD：23~80℃ | 7.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric constant | |||
| 1 MHz | 3.50 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 0.026 | IEC 60250 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | < 80 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Processing (melt) temperature | 250 to 270 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Injection speed | Moderate-Fast | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0,005 g/ml H2SO4 |
| 3. 0.079 in/min |
| 4. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |