| About |
|---|
| Acrylic Coated Film Biaxially oriented polypropylene (BOPP) film coated on both sides with an aqueous acrylic (chlorine free) dispersion. RC200/240 are suitable for heavy duty applications where the films’ excellent hot-tack and seal threshold can give superior machine performance over alternative structures.&& |
| Product Description | |
|---|---|
| Generic | PP Alloy |
| Material Status | Commercial: Active |
| Features | Good heat sealing,High impact resistance,Optical performance,High anti-blocking,Retention of aroma ,Food contact compliance,Thermal viscous strength,Moisture resistance,low-temperature impact resistance,Puncture Resistant,Low temperature heat sealing |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Shrinkage rate | Internal Method | ||
| MD：121℃，1 min | 2.0 | % | Internal Method |
| MD：129℃，1 min | 7.0 | % | Internal Method |
| TD：129℃，1 min | 1.0 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | ASTM D1894 | ||
| With oneself – dynamic | 0.25 | ASTM D1894 | |
| With oneself – static | 0.25 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Sealing emphasis | 0.15 | N/mm | Internal Method |
| Initial sealing temperature | 85.0 to 146 | ℃ | Internal Method |
| Oxygen permeability | |||
| 25℃，0% RH | 15 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water vapor transmittance | |||
| 38℃，90% RH | 3.1 | g/m²/24 hr | ASTM F1770 |
| film thickness | 240 | Internal Method | |
| dosage | 21.1 | m²/kg | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45° | 95 | ASTM D2457 | |
| Haze | 1.5 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 265°F; 2secs; 15psi |
| 3. 2secs; 15psi |
| 4. Wide angle; 2.5° |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |