| About |
|---|
| Multi-Purpose Film Biaxially oriented polypropylene (BOPP) film co-extruded on both sides with polyolefinic copolymers. RGP is a is a multi-purpose film suitable for packaging a wide range of products either in single web form, or in a lamination to itself or to other substrates. RGP100 and RGP120 are suitable for both overwrapping and form-fill-and-seal applications.&& |
| Product Description | |
|---|---|
| Generic | PP Alloy |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good heat sealing,High impact resistance,Good Printability,Food contact compliance,Poor moisture permeability,Antistatic property,low-temperature impact resistance,Puncture Resistant |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Shrinkage rate | Internal Method | ||
| MD：129℃，1 min | 6.0 | % | |
| TD：129℃，1 min | -1.0 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | ASTM D1894 | ||
| With oneself – dynamic, outer/outer layers | 0.30 | ||
| Compared to itself – static, outer/outer layers | 0.30 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 3000 | µm | |
| Secant modulus | ASTM D882 | ||
| 1% secant, MD | 2490 | MPa | |
| 1% secant, TD | 2090 | MPa | |
| tensile strength | ASTM D882 | ||
| MD, yield | 230 | MPa | |
| TD, yield | 190 | MPa | |
| Tensile strain | ASTM D882 | ||
| MD, fracture | 90 | % | |
| TD, fracture | 130 | % | |
| Sealing emphasis | 0.14 | N/mm | Internal Method |
| Initial sealing temperature | 116 to 146 | ℃ | Internal Method |
| Oxygen permeability | |||
| 23℃，0% RH | 41 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water vapor transmittance | |||
| 38℃，90% RH | 5.0 | g/m²/24 hr | ASTM F1770 |
| Corona Treatment | 38 | dyne/cm | Internal Method |
| dosage | 36.7 | m²/kg | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45° | 100 | ASTM D2457 | |
| Haze | 2.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10%/min |
| 3. 50%/min |
| 4. 225°F; 1sec; 15lb/in²; untreated to untreated |
| 5. 2secs; 15lb/in²; untreated to untreated |
| 6. Wide angle; 2.5° |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |