Propylux® HS - SOLIAO

About
Medical grade Propylux HS is made from an FDA approved polypropylene resin. Through a unique heat-stabilizing process, the extruded material is able to withstand higher temperatures with less water absorption than standard polypropylene. Recommended sterilization techniques for Propylux HS include steam autoclaving and cold sterilization. Advantages: Excellent Chemical Resistance Laser Markable Lot controlled and traceable Low moisture absorption FDA Resin Superior Dimensional Stability Applications: Provisional Trials Cranio-maxillofacial trays Sterilization tray components&&

About

Medical grade Propylux HS is made from an FDA approved polypropylene resin. Through a unique heat-stabilizing process, the extruded material is able to withstand higher temperatures with less water absorption than standard polypropylene. Recommended sterilization techniques for Propylux HS include steam autoclaving and cold sterilization. Advantages: Excellent Chemical Resistance Laser Markable Lot controlled and traceable Low moisture absorption FDA Resin Superior Dimensional Stability Applications: Provisional Trials Cranio-maxillofacial trays Sterilization tray components&&

Product Description
Supplier	Westlake Plastics
Generic	PP not specified
Material Status	Commercial: Active
Features	Good Dimensional Stability,High pressure disinfection,High Heat Resistance,Solvent resistance,High pressure heat resistance,Laser engraving,Low moisture absorption,Heat Stabilized,HB
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.920	g/cm³	ASTM D792
Water absorption rate
24hr	0.025	%	ASTM D570

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	80	J/m	ASTM D256
Notched impact strength of cantilever beam	1100	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature			ASTM D648
0.45 MPa, unannealed	152	℃	ASTM D648
1.8 MPa, unannealed	80.0	℃	ASTM D648
Linear coefficient of thermal expansion
MD	8.3E-5	1/℃	ASTM D696

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB		UL 94

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	101		ASTM D785
Tensile modulus	2200	MPa	ASTM D638
tensile strength			ASTM D638
yield	36.6	MPa	ASTM D638
fracture	30.1	MPa	ASTM D638
Tensile strain			ASTM D638
yield	10	%	ASTM D638
fracture	40	%	ASTM D638
Bending modulus	2160	MPa	ASTM D790
bending strength	63.9	MPa	ASTM D790
compressive strength	55.2	MPa	ASTM D695

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.