| PROTEQ™ C15ST4L is a medium flow, impact modified, 20% talc filled, heat stabilised grade of polypropylene copolymer. It is intended for use in applications where relatively higher impact resistance and heat age stability is required. Note: The letter “U” indicate UV stabilisation has been added [ ie: PROTEQ™ C15UST4 ].&& |
| Product Description | |
|---|---|
| Supplier | Qenos |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good heat aging resistance,High impact resistance,Moderate liquidity,Copolymer,Heat Stabilized,HB |
| Availabilitys | North America,Latin America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 12 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.0 mm | 1.2 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 75 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 3.2 mm | 680 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm | 126 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 68.0 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 7.5E-5 | 1/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 | |
| Igniting temperature of the hot wire | |||
| 1.6 mm | 550 | ℃ | AS/NZS 60695 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shaw’s D | 70 | ISO 868 | |
| Shore D, 15 seconds | 62 | ISO 868 | |
| tensile strength | |||
| 3.20 mm | 26.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 50 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 2150 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm | 43.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 85 to 90 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 195 to 215 | °C | |
| Barrel middle temperature | 205 to 225 | °C | |
| Barrel front temperature | 215 to 235 | °C | |
| Processing (melt) temperature | 220 to 270 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Injection pressure | 60.0 to 140 | MPa | |
| Injection speed | 中等 | ||
| Back pressure | 0.100 to 0.500 | MPa | |
| Screw speed | 40 to 60 | rpm | |
| Clamping force | 3.0 to 6.0 | kN/cm² | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |