| About |
|---|
| PTS PCA-2201NHV is a Polycarbonate + ABS (PC+ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include: Flame Rated Flame Retardant Halogen Free UV Stabilized&& |
| Product Description | |
|---|---|
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,V-0,5VA,5VB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 230℃，3.80kg | 12 | g/10min | ASTM D1238 |
| 260℃，2.16kg | 16 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.60 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 3.17 mm | 60.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.17 mm | 65 | % | ASTM D638 |
| Bending modulus | |||
| 3.17 mm | 2690 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 3.17 mm | 88.9 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 590 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 85.0 | ℃ | ASTM D648 |
| Relative temperature index | 60.0 | ℃ | UL 746 |
| Electrical performance | 60.0 | ℃ | UL 746 |
| Impact mechanical performance | 60.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 18 | kV/mm | ASTM D149 |
| Compared to the leakage tracing index | > 600 | V | UL 746 |
| Compared to the leakage tracing index | PLC 0 | UL 746 | |
| High Arc Burning Index (HAI) | UL 746 | ||
| 1.50 mm | 60.0 to 120 | UL 746 | |
| 2.50 mm | 60.0 to 120 | UL 746 | |
| 3.00 mm | 60.0 to 120 | UL 746 | |
| High Arc Burning Index (HAI) | UL 746 | ||
| 1.5 mm | PLC 1 | UL 746 | |
| 2.5 mm | PLC 1 | UL 746 | |
| 3.0 mm | PLC 1 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 3 | UL 746 | |
| HVTR | 80.0 to 150 | mm/min | UL 746 |
| 1.50 mm | 15 to 30 | sec | UL 746 |
| 2.50 mm | 15 to 30 | sec | UL 746 |
| 3.00 mm | 30 to 60 | sec | UL 746 |
| Hot wire ignition | |||
| HWI | UL 746 | ||
| HWI | UL 746 | ||
| 1.5 mm | PLC 3 | UL 746 | |
| 2.5 mm | PLC 3 | UL 746 | |
| 3.0 mm | PLC 2 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 2.00 mm | 5VB | UL 94 | |
| 2.50 mm | 5VA | UL 94 | |
| 3.00 mm | 5VA | UL 94 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 1.5 mm | 925 | ℃ | IEC 60695-2-12 |
| 2.0 mm | 925 | ℃ | IEC 60695-2-12 |
| 3.0 mm | 950 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 1.5 mm | 700 | ℃ | IEC 60695-2-13 |
| 2 mm | 700 | ℃ | IEC 60695-2-13 |
| 3 mm | 700 | ℃ | IEC 60695-2-13 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |